Title: Estudo tribológico do revestimento de Stellite 6, Aspergido por HVOF antes e após polimento, e do substrato de aço inoxidável AISI 304
metadata.dc.creator: Rodrigues, Pedro Henrique Eça
metadata.dc.contributor.advisor1: Oliveira, Ana Claudia Costa de
metadata.dc.description.resumo: Com a evolução mecânica cresceu, também, a necessidade de melhoria contínua de componentes mecânicos. Desta forma, alguns problemas são enfrentados com certa frequência, tendo como exemplo este trabalho, o desgaste de componentes mecânicos causados pela interação entre diferentes materiais. Com a necessidade de se obter uma superfície que acresça a vida útil de peças e componentes de máquinas e que possua propriedades mecânicas que sejam resistentes ao desgaste abrasivo, revestiu-se uma superfície por aspersão térmica através do método de deposição HVOF (do inglês High Velocity Oxygen Fuel) com uma liga de cobalto, comercialmente conhecida como Stellite 6. Esse revestimento, com uma dureza maior que o substrato, caracteriza-se por sua alta resistência aos desgastes, aqui dando ênfase à abrasão. Este possui uma estrutura densa, com baixo nível de porosidade e um bom ancoramento ao substrato. As amostras revestidas foram analisadas através de Microscopia Eletrônica de Varredura (MEV), para verificar e qualificar a qualidade do revestimento, análise de microdureza, teste de desgaste e teste de rugosidade. Os ensaios e análises mostraram que as amostras revestidas de Stellite 6 apresentaram melhor desempenho nos testes de microdureza, desgaste e rugosidade (desde que polidas) em relação as amostras do substrato de aço inoxidável AISI 304.
Abstract: With the increasing mechanical evolution, there has also been a need for continuous improvement of mechanical components. In this way, some problems are faced with a certain frequency, as an example we have the theme of this work, the wear of mechanical components caused by the interaction between different materials. With the need to obtain a surface that increases the useful life of parts and components of machines and which possesses mechanical properties that are resistant to the abrasive wear, a surface by thermal spraying was coated by the HVOF deposition method (High Velocity Oxygen Fuel) with a cobalt alloy, commercially known as Stellite 6. This coating, with a higher hardness than the substrate, is characterized by its high wear resistance, here emphasizing abrasion. It has a dense structure, with a low level of porosity and a good anchoring to the substrate. The coated samples were analyzed by Scanning Electron Microscopy (SEM) to verify and qualify coating quality, microhardness analysis, wear test and rough’ness test. The tests and analyzes showed that the Stellite 6 coated samples showed better performance in the microhardness, wear and roughness tests (if polished) compared to the AISI 304 stainless steel substrate samples.
Keywords: Engenharia mecânica
Desgaste abrasivo
Aspersão térmica
Revestimentos
Stellite 6
Mechanical engineering
Abrasive wear
Thermal spraying
Coating
metadata.dc.subject.cnpq: CNPQ::ENGENHARIAS
metadata.dc.language: por
metadata.dc.publisher.country: Brasil
Publisher: Universidade Federal do Pampa
metadata.dc.publisher.initials: UNIPAMPA
metadata.dc.publisher.department: Campus Alegrete
Citation: RODRIGUES, Pedro Henrique Eça. Estudo tribológico do revestimento de Stellite 6, Aspergido por HVOF antes e após polimento, e do substrato de aço inoxidável AISI 304. 54 p. 2018. Trabalho de Conclusão de Curso (Graduação em Engenharia Mecânica) – Universidade Federal do Pampa, Campus Alegrete, Alegrete, 2018.
metadata.dc.rights: Acesso Aberto
URI: http://dspace.unipampa.edu.br:8080/jspui/handle/riu/3345
Issue Date: 29-Jun-2018
Appears in Collections:Engenharia Mecânica

Files in This Item:
File Description SizeFormat 
PEDRO HENRIQUE EÇA RODRIGUES 2018.pdf1,86 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.