Título : Autocicatrização de concretos com uso de aditivo cristalizante
Autor(es): Tambara, Rafael Fumaco
Primeiro Orientador: Costa, Fernanda Bianchi Pereira da
Coorientador: Venquiaruto, Simone Dornelles
Resumo: Este trabalho investigou a influência da incorporação de um aditivo cristalizante nacional no fenômeno da autocicatrização de concretos estruturais produzidos com cimento Portland (CP V ARI – RS) e submetidos a pré-carregamentos por compressão axial em diferentes idades (7 e 28 dias). Para cada idade de carregamento foram rompidas até o limite três amostras de cada traço e a partir do valor médio de ruptura foi determinado o percentual de carga que seriam aplicados em parte dos concretos (0%, 50% e 80% do fck,méd). Visando estimular a autocicatrização, as amostras permaneceram em cura submersa desde a sua produção até as suas respectivas idades de ensaio, sendo retiradas da cura apenas para a etapa de pré-carregamento e posteriormente retornando para a mesma. As amostras pré-carregadas aos 7 dias foram ensaiadas aos 14, 28, 56 e 91 dias, enquanto que as amostras pré-carregadas aos 28 dias foram ensaiadas aos 35, 56 e 91 dias. Os ensaios de controle selecionados foram de Resistência à Compressão Axial, Absorção de Água por Capilaridade (Método de Kelham) e Velocidade de Propagação de Onda Ultrassônica. Além disso, algumas amostras foram analisadas por meio de imagens de Microscopia Óptica para monitorar a formação dos produtos de autocicatrização ao longo do tempo. Os resultados obtidos permitem concluir que: (i) através do ensaio de resistência à compressão axial constatou-se que os concretos com aditivo cristalizante (CA) sem aplicação de carregamento apresentaram um melhor desempenho mecânico entre as misturas investigadas; (ii) a avaliação da velocidade de propagação de onda ultrassônica com a variação do tempo mostrou um aumento da velocidade ultrassônica nos concretos com incorporação de CA e pré-carregados nas idades de 7 e 28 dias, independentemente do percentual de carregamento aplicado (0%, 50% e 80%), indicando a reparação das microfissuras; (iii) quanto a absorção de água por capilaridade, os concretos que não foram submetidos a pré-carregamento exibiram padrões semelhantes de redução na absorção média, independentemente da presença do aditivo cristalizante. No entanto, destaca-se que o concreto com adição de CA demonstrou uma resistência superior à absorção de água em comparação com o concreto de referência, especialmente sob condições de pré-carregamento; (iv) para análise de imagem por microscopia óptica os concretos referência não apresentaram cicatrização superficial relevante, enquanto que os concretos com adição de CA apresentaram preenchimento parcial das fissuras, por meio da precipitação do carbonato de cálcio. Em suma, os ensaios realizados nesta pesquisa corroboram os benefícios da adição de aditivo cristalizante aos concretos, especialmente no que diz respeito à capacidade de autocicatrização.
Resumen : This study investigated the influence of the incorporation of a crystalline admixture (CA) on self-healing in structural concretes made with Portland cement (CP-V ARI-RS) and subjected to pre-loading by axial compression at different ages (7 and 28 days). For each loading age, three samples of each mix were tested for compressive strength, and the average rupture value was used to determine the percentage of load that would be applied to the concrete (0%, 50%, and 80% of the average fck). To stimulate self-healing, the samples were submerged in water from when they were produced until their respective test ages. The samples were only removed from curing during the pre-loading stage. Samples preloaded at 7 days were tested at 14, 28, 56, and 91 days, while samples preloaded at 28 days were tested at 35, 56, and 91 days. The control tests selected were axial compressive strength, water absorption by capillarity (Kelham method), and ultrasonic wave propagation velocity. In addition, some samples were analyzed using optical microscopy images to monitor the formation of self-healing products over time. The results obtained allow us to conclude that (i) the axial compressive strength test showed that concrete with CA and without loading had the best mechanical performance of the mixtures investigated; (ii) the evaluation of ultrasonic wave propagation velocity with time variation showed an increase in ultrasonic velocity in concretes incorporating CA and preloaded at 7 and 28 days, regardless of the percentage of loading applied (0%, 50% and 80%), indicating the repair of microcracks; (iii) concretes that were not preloaded showed similar patterns of reduction in average values of water absorption capillarity, regardless of the presence of the crystalline admixture. However, it is noteworthy that the concrete with added CA showed superior resistance to water absorption compared to the reference concrete, especially under pre-loading conditions; (iv) for optical microscopy image analysis, the reference concretes showed no significant surface healing, while the concretes with added CA showed partial filling of the cracks through the precipitation of calcium carbonate. In short, the tests carried out in this research corroborate the benefits of adding a crystalline admixture to concrete, especially its ability to self-heal.
Palabras clave : Engenharia
Aditivo cristalizante
Concreto
Engineering
Crystallizing additive
Concrete
CNPQ: CNPQ::ENGENHARIAS
Idioma: por
metadata.dc.publisher.country: Brasil
Editorial : Universidade Federal do Pampa
Sigla da Instituição: UNIPAMPA
Campus: Campus Alegrete
Curso: Mestrado Acadêmico em Engenharia
Citación : TAMBARA, Rafael Fumaco. Autocicatrização de concretos com uso de aditivo cristalizante. 167p. 2024. Orientadora: Fernanda Bianchi Pereira da Costa. Dissertação (Mestrado em Engenharia) – Universidade Federal do Pampa, Campus Alegrete, 2024.
Tipo de acesso: Acesso Aberto
URI : https://repositorio.unipampa.edu.br/jspui/handle/riu/9469
Fecha de publicación : 18-jul-2024
Aparece en las colecciones: Mestrado em Engenharia

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
Dissertação - Rafael Fumaco Tambara - 2024.pdf38.63 MBAdobe PDFVisualizar/Abrir


Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.