Title: Comportamento corrosivo de soldas à fricção FSW do tipo alumínio-cobre
metadata.dc.creator: Arrussul, Vitor Godoy
metadata.dc.contributor.advisor1: Wiedenhöft, Aldoni Gabriel
metadata.dc.description.resumo: 3-Glicidoxipropil-trimetoxi-silano foi utilizado como um método preventivo no controle da corrosão em ligas de alumínio AA6060-T5 e em ligas de cobre Cu ASTM-B110, bem como suas juntas soldadas por fricção ( do inglês friction stir welding - FSW). As amostras de AA 6060-T5/Cu ASTM-B110 soldadas à fricção foram cortadas utilizando-se uma máquina de precisão ISOMET 2000 e atacadas com duas soluções diferentes: uma contendo H2O:NH4OH:H2O2 (0.45:0.45:0.1 v/v) na superfície da junta de Cu ASTM-B-110 e a outra contendo 0.5% (v/v) HF na superfície da junta de AA 6060-T5. Uma eficiente região de mistura entre AA 6060-T5 e Cu ASTM-B110 foi observada na zona de mistura (do inglês weld nugget zone – WNZ) conforme observações por microscopia ótica. O efeito do 3-Glixidoxipropil-trimetoxi-silano depositado sobre a superfície destes materiais e seguida da imersão destes em solução de NaCl 0,05 mol L-1 NaCl foi investigado por testes eletroquímicos. Os resultados, principalmente o comportamento indutivo nas baixas frequências, indicam que o revestimento da superfície das ligas de AA6060-T5, das ligas de Cu ASTM-B110 e da junta soldada AA6060-T5/Cu ASTM-B110 com 3- Glixidoxipropil-trimetoxi-silano leva a uma diminuição na velocidade de corrosão comparada as amostras não revestidas. Este fato caracteriza que este tratamento pode ser uma eficiente alternativa para retardar processos corrosivos, particularmente a forte corrosão galvânica que comumente ocorre em juntas soldadas a fricção do tipo AA6060-T5/CuASTM-B110.
Abstract: 3-Glycidoxypropyl-trimethoxy-silane was used as a preventive measure for corrosion control in 6060-T5 aluminum alloy (AA 6060-T5) and ASTM-B110 copper (Cu ASTM-B110) joined by friction stir welding (FSW). The substrates of the AA 6060-T5/Cu ASTM-B110 stir welding joint were cut using a precision cutting machine (ISOMET 2000) and etched with two different solutions: H2O: NH4OH:H2O2 (0.45: 0.45: 0.1 v/v) at the Cu ASTM-B-110 joint surface and 0.5% (v/v) HF at the AA 6060-T5 joint. A good mixing of AA 6060-T5 and Cu ASTM-B110 was observed in the weld nugget zone (WNZ) according to observations by optical microscopy. The effect of the 3-glycidoxypropyl-trimethoxy-silane deposited on the surfaces of these materials following immersion in 0.05 mol L-1 NaCl was investigated by electrochemical methods. The results, mainly the inductive behavior at low frequencies, show that the coating of the alloys AA 6060-T5 and Cu ASTM-B110, and the welding joint (AA 6060-T5/Cu ASTM-B110) with 3-glycidoxypropyl-trimethoxy-silane leads to a decrease in the corrosion rate on exposure to a chloride solution in comparison with non-coated materials. This feature characterizes this treatment as an alternative approach to retarding corrosion processes, particularly the strong galvanic corrosion that commonly occurs at the AA 6060-T5/Cu ASTM-B110 welding joint.
Keywords: Mechanical Engineering
Aluminum
Copper
Corrosion
metadata.dc.subject.cnpq: CNPQ::ENGENHARIAS
Publisher: Universidade Federal do Pampa
metadata.dc.rights: Attribution-NonCommercial-NoDerivs 3.0 Brazil
metadata.dc.rights.uri: http://creativecommons.org/licenses/by-nc-nd/3.0/br/
URI: http://hdl.handle.net/riu/931
Issue Date: 30-Nov-2015
Appears in Collections:Engenharia Mecânica

Files in This Item:
File Description SizeFormat 
Comportamento corrosivo de soldas à fricção FSW do tipo alumínio-cobre.pdf1,78 MBAdobe PDFView/Open


This item is licensed under a Creative Commons License Creative Commons