metadata.dc.type: Trabalho de Conclusão de Curso
Title: Estudo do comportamento reológico no tempo de argamassas com substituição de sílica de casca de arroz
metadata.dc.creator: Cortese, Nadine
metadata.dc.contributor.advisor1: Marangon, Ederli
metadata.dc.contributor.advisor-co1: Oliveira, Marcelo de Jesus Dias de
metadata.dc.description.resumo: Nessa pesquisa foram avaliadas as propriedades e características de argamassas no estado fresco em diferentes intervalos de tempo e velocidades de ensaio, com substituições de cimento Portland por sílica de casca de arroz (SCA). A análise foi feita a partir de um traço referência onde foram feitas substituições em massa de cimento Portland por SCA em 5, 10, 15, 20 e 30%, com a relação água/cimento fixada em 0,71. Para a análise do comportamento reológico das argamassas foram realizados os ensaios de mesa de consistência (Flow Table), densidade da massa e teor de ar incorporado logo após a produção da mistura, e o Vicat Modificado e Squeeze Flow nas idades de 15, 60, 120 e 180 minutos. O ensaio de Squeeze Flow também foi realizado para diferentes velocidades (1mm/min, 0,1mm/s e 1mm/s). Os resultados obtidos pelos ensaios de consistência (Flow Table e Vicat Modificado) diminuíram conforme aumentou-se a porcentagem de SCA. Com o avanço da idade, os resultados no ensaio de Vicat Modificado, demostraram que a penetração do cone diminui, pelo fato da sílica absorver a água da mistura, deixando-a seca. Para os ensaios físicos de densidade de massa e o teor de ar incorporado, os resultados não apresentaram alterações significativas com inclusão da SCA. No ensaio de Squeeze Flow os dados sugerem uma melhora na trabalhabilidade da argamassa com substituição de 5% na mistura em relação ao traço referência, porém esse comportamento não se repete nas idades posteriores. Ainda, pode ser observado que o deslocamento diminuiu e a rigidez aumentou. A tensão de escoamento das misturas e a viscosidade variam de acordo com a velocidade de ensaio. Velocidades mais elevadas, como a ensaiada de 1mm/s, não são viáveis para a análise dos dados do Squeeze Flow, pelo fato de que o comportamento elástico da argamassa é muito pequeno. Os valores de tração máxima aumentaram com o avanço da idade e quanto maior a porcentagem de sílica presente na mistura.
Abstract: In this research, the properties and characteristics of mortar in fresh state were evaluated at different time intervals and at different test speeds, with substitutions of Portland cement with rice husk silica (SCA). The analysis was done from a reference trace where mass substitutions of Portland cement by SCA were made in 5, 10, 15, 20 and 30%, with the water/cement ratio fixed at 0.71. For the analysis of the rheological behavior of the mortars, the tests of consistency table (Flow Table), density of the mass and air content incorporated soon after the production of the mixture, and the modified Vicat and Squeeze Flow in the ages of 15, 60, 120 and 180 minutes. The Squeeze Flow test was also performed for different speeds (1mm/min, 0,1mm/s and 1mm/s). The results obtained by the consistency tests (Flow Table and modified Vicat) decreased as the percentage of ACS was increased. With advancing age, the results in the modified Vicat assay showed that the penetration of the cone decreases, because the silica absorbs the water of the mixture, leaving it dry. For the physical assays of mass density and the incorporated air content, the results did not present significant alterations with inclusion of ACS. In the Squeeze Flow test the data suggest an improvement in the workability of the mortar with a 5% substitution in the mixture in relation to the reference trait, but this behavior does not repeat in later ages. Further, it can be seen that the displacement decreased and the stiffness increased. The flow stress of the mixtures and the viscosity will vary according to the test speed. Higher velocities, such as the 1mm/s test, are not feasible for analyzing the Squeeze Flow data, because the elastic behavior of the mortar is very small. The values of maximum traction increased with the advancement of age and the higher the percentage of silica present in the mixture.
Keywords: Engenharia civil
Argamassa
Reologia
Sílica da casca de arroz
Squeeze Flow
Civil engineering
Mortar
Rheology
Rice husk silica
metadata.dc.subject.cnpq: CNPQ::ENGENHARIAS
metadata.dc.language: por
metadata.dc.publisher.country: Brasil
Publisher: Universidade Federal do Pampa
metadata.dc.publisher.initials: UNIPAMPA
metadata.dc.publisher.department: Campus Alegrete
Citation: CORTESE, Nadine. Estudo do comportamento reológico no tempo de argamassas com substituição de sílica de casca de arroz. Orientador: Ederli Marangon. 2019. 69 p. Trabalho de Conclusão de Curso (Bacharel em Engenharia Civil) - Universidade Federal do Pampa, Curso de Engenharia Civil, Alegrete, 2019.
metadata.dc.rights: Acesso Aberto
URI: http://dspace.unipampa.edu.br:8080/jspui/handle/riu/4198
Issue Date: 27-Jun-2019
Appears in Collections:Engenharia Civil

Files in This Item:
File Description SizeFormat 
Nadine Cortese - 2019.pdf4,91 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.