metadata.dc.type: Trabalho de Conclusão de Curso
Title: Análise da resistência a corrosão em aços ferramenta
metadata.dc.creator: Dallago, Lucas
metadata.dc.contributor.advisor1: Oliveira, Ana Claudia Costa de
metadata.dc.contributor.advisor-co1: Santos, Hortencia Noronha dos
metadata.dc.description.resumo: Os aços ferramenta são de grande importância na indústria mecânica, variando suas aplicações desde matrizes, moldes e brocas até equipamentos mais complexos. Esses aços são empregados geralmente em situações e ambientes de extrema solicitação tais como, ferramentas de corte, necessitando alta resistência a deformação e temperatura. Duas amostras de aço ferramenta, sendo uma delas do tipo P20TS modificado, com reduzido teor de carbono resultando numa maior homogeneidade superficial, e outra um aço em desenvolvimento, ambos produzidos pela empresa Villares Metals de Sumaré/SP, com a nomenclatura de VP20TS e Hardmax 500 respectivamente, foram submetidas a ensaios de corrosão eletroquímica através do levantamento de curvas de polarização potenciodinâmicas, curvas de potencial com tempo e testes de dureza (antes e após corrosão), com a finalidade de comparar a resistência a corrosão entre elas. Para os ensaios em que foram levantadas as curvas, usando potenciostato, foi estipulado a duração de 1800 segundos, com uma velocidade de varredura de 1mV.s-1, em meio corrosivo (eletrólito) de NaCl 3,5% aerado. A área submetida aos testes corrosivos e o eletrólito foram padronizados em 0,283 cm2 (0,6cm de diâmetro) e 105ml. Os resultados obtidos mostram que o aço VP20TS possui melhor resistência a corrosão, com uma densidade de corrente menor em relação ao Hardmax 500, observadas pela corrente de corrosão (Icorr) sendo 6,67μA contra 8,61μA respectivamente, com relação a afinidade dos aços a corroer, característica definida pelo potencial de corrosão (Ecorr), ambos apresentaram valores muito próximos indicando comportamento parecido neste quesito.
Abstract: Tool steels have great importance in the mechanical industry, varying their applications from matrices, molds and drills to more complex equipments. These steels are usually used in situations and environments of extreme solicitation such as cutting tools, requiring high resistance to deformation and temperature. Two samples of tool steel, one P20 modified and another steel in development, both produced by the company Villares Metals de Sumaré/SP, with the nomenclature of VP20TS and Hardmax 500 respectively, were subjected to eletrochemical corrosion tests according to potentiodynamic polarization curves, potential curves versus time and hardness tests (before and after corrosion), with the purpose of comparing the corrosion resistance between them. For the tests in which the curves were raised, using potentiostat, the duration of 1800 seconds was stipulated, with a scanning speed of 1mV.s-1, in corrosive environment (electrolyte) of NaCl 3,5%, aerated. The area subjected to the corrosive tests and the electrolyte were standardized in 0.283 cm2 (6mm diameter) and 105ml. The results obtained show that the VP20TS Steel has better corrosion resistance, with a lower current density compared to the Hardmax 500, observed by the corrosion current (Icorr) being 6.67 μA against 8.61 μA respectively, in relation to the susceptibility of steels to corrode, characteristic defined by the corrosion potential (ICorr), both showed very close values indicating similar behavior in this item.
Keywords: Engenharia mecânica
Corrosão
Aço ferramenta
Curva de polarização
Mechanical engineering
Corrosion
Tool steel
Polarization curve
metadata.dc.subject.cnpq: CNPQ::ENGENHARIAS
metadata.dc.language: por
metadata.dc.publisher.country: Brasil
Publisher: Universidade Federal do Pampa
metadata.dc.publisher.initials: UNIPAMPA
metadata.dc.publisher.department: Campus Alegrete
Citation: DALLAGO, Lucas. Análise da resistência a corrosão em aços ferramenta. Orientador: Ana Claudia Costa de Oliveira. 2019. 58 p. Trabalho de Conclusão de Curso (Bacharel em Engenharia Mecânica) - Universidade Federal do Pampa, Curso de Engenharia Mecânica, Alegrete, 2019.
metadata.dc.rights: Acesso Aberto
URI: http://dspace.unipampa.edu.br:8080/jspui/handle/riu/4182
Issue Date: 8-Jul-2019
Appears in Collections:Engenharia Mecânica

Files in This Item:
File Description SizeFormat 
Lucas Dallago - 2019.pdf2,9 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.