Title: Estudo tribológico dos revestimentos de Fe-29Cr-4B-1,75Si E WC- 10Co-4Cr por aspersão térmica para redução do desgaste abrasivo e erosivo resultante da ação do grão de arroz
metadata.dc.creator: Panziera, Renato Camponogara
metadata.dc.contributor.advisor1: Tier, Marco Antônio Durlo
metadata.dc.contributor.advisor-co1: Oliveira, Ana Claudia Costa de
metadata.dc.description.resumo: A produção do arroz é a terceira maior do mundo dentre seis mil espécies de cereais estando atrás apenas do milho e do trigo. Componentes de máquinas que trabalham sob o contato direto com o grão de arroz sofrem desgaste severo devido à natureza abrasiva de sua casca. Dessa forma, o objetivo principal deste estudo é investigar o comportamento tribológico do revestimento de Fe-29Cr-4B-1.75Si aspergido pelo método de arco elétrico com arame e do revestimento de WC-10Co-4Cr aspergido pelo método high velocity oxygen fuel - HVOF, ambos em substrato de aço carbono SAE 1016. Foram realizados o ensaio de desgaste abrasivo utilizando a norma ASTM G65 que utiliza areia como abrasivo e uma variação empregando a casca de arroz como material abrasivo. Além disso, foi investigado o comportamento tribológico in situ dos revestimentos em uma estrutura de secagem de arroz com capacidade de processamento de 70 t/h. Os revestimentos foram caracterizados por microscopia eletrônica de varredura (MEV), difração de raios-X e microdureza. Como resultado principal percebeu-se que o revestimento com maior microdureza (WC-10Co-4Cr) apresentou as menores taxas de desgaste durante os ensaios. Analisando os mecanismos de desgaste sob os revestimentos e substrato, ao utilizar a areia como material abrasivo (ensaio ASTM G65), o material foi removido por riscamento enquanto ao utilizar a casca de arroz o mecanismo de desgaste ocorreu por microcortes. Outro ponto importante foi o fato de as amostras terem sofrido elevada perda de volume por desgaste erosivo ao serem submetidas ao desgaste dentro da estrutura de secagem de arroz, in situ.
Abstract: Rice production is the third largest in the world out of six thousand species of cereals being behind only corn and wheat. Components of machines that work under direct contact with rice grain suffer severe wear due to the abrasive nature of their husk. Thus, the main objective of this study is to investigate the tribological behavior of the Fe-29Cr-4B-1.75Si coating sprayed by the electric arc with wire method and the WC-10Co-4Cr coating sprayed by the high velocity oxygen fuel - HVOF, both on SAE 1016 carbon steel substrate. The abrasive wear test was performed using ASTM G65 standard which uses sand as an abrasive and a variation employing the rice husk as an abrasive material. Furthermore, the in situ tribological behavior of the coatings in a rice drying structure with processing capacity of 70 t/h was investigated. The coatings were characterized by scanning electron microscopy (SEM), X-ray diffraction and microhardness. As a main result it was noticed that the coating with higher microhardness (WC-10Co-4Cr) showed the lowest wear rates during the tests. Analyzing the wear mechanisms under the coatings and substrate when using the sand as an abrasive material (ASTM G65 test), the material was removed by scratches while using the rice husk the mechanism of wear occurred by micro cuts. Another important point was the fact that the samples suffered a high loss of volume due to erosive wear when subjected to wear inside the rice drying structure, in situ.
Keywords: Engenharia
Arroz
Cascas (Engenharia)
Desgaste
Revestimentos
Tribologia
Engineering
Shells (Engineering)
Tribology
Rice
Wear
Coatings
metadata.dc.subject.cnpq: CNPQ::ENGENHARIAS
metadata.dc.language: por
metadata.dc.publisher.country: Brasil
Publisher: Universidade Federal do Pampa
metadata.dc.publisher.initials: UNIPAMPA
metadata.dc.publisher.department: Campus Alegrete
metadata.dc.publisher.program: Mestrado Acadêmico em Engenharia
Citation: PANZIERA, Renato Camponogara. Estudo tribológico dos revestimentos de Fe-29Cr-4B-1,75Si E WC- 10Co-4Cr por aspersão térmica para redução do desgaste abrasivo e erosivo resultante da ação do grão de arroz. Orientador: Marco Antônio Durlo Tier. 2019. 73p. Dissertação (Mestrado em Engenharia) – Universidade Federal do Pampa, Campus Alegrete, Alegrete, 2019.
metadata.dc.rights: Acesso Aberto
URI: http://dspace.unipampa.edu.br:8080/jspui/handle/riu/3996
Issue Date: 4-Apr-2019
Appears in Collections:Mestrado em Engenharia

Files in This Item:
File Description SizeFormat 
Renato Camponogara Panziera - 2019.pdf4,26 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.