Title: Resistência à cavitação do revestimento de carbeto de tungstênio refundido via laser de CO2 aplicado em aço AISI 1020
metadata.dc.creator: Ronzani, Antonio Guilherme
metadata.dc.contributor.advisor1: Oliveira, Ana Claudia Costa de
metadata.dc.contributor.advisor-co1: Carotenuto, Adriano Roberto da Silva
metadata.dc.description.resumo: Em engenharia mecânica são grandes as preocupações com a cavitação, assim como a abrasão de sedimentos transportados pelo fluído em instalações hidráulicas, bombas e turbinas, sobretudo devido aos prejuízos que estes fenômenos podem causar nas estações elevatórias e usinas hidrelétricas. Estudam-se diversas propostas para a eliminação ou redução deste problema, desde o redesign do componente e sua instalação, até a aplicação de revestimentos superficiais com materiais de alta tecnologia. O objetivo geral deste trabalho é fazer a caracterização e análise tribológica de cavitação em amostras de aço AISI 1020, revestidas por aspersão térmica com Carbeto de Tungstênio e posteriormente irradiadas via Laser de CO2. As amostras foram analisadas por MEV/EDS, Microscopia Ótica, Rugosímetro, Micro Durômetro e teste de resistência à cavitação. Os resultados foram uma ligação metalúrgica entre revestimento e substrato, além de uma densificação e endurecimento superficial do revestimento devido à refusão via Laser de CO2; a análise por EDS do substrato e seu revestimento, mostram a evaporação de elementos mais voláteis como Cromo e Cobalto no momento da irradiação do Laser e confirma a difusão de elementos químicos do revestimento no substrato; ocorreu a diminuição da rugosidade superficial após a aspersão térmica. O teste de cavitação comprova uma resistência à erosão, mostrando-se superior a materiais comerciais.
Abstract: Mechanical engineering is concerned with cavitation as well as the abrasion of sediments carried by the fluid in hydraulic installations, pumps and turbines, mainly due to the damages that these phenomena can cause in the elevators and hydroelectric plants. Proposals for the elimination or reduction of this problem are studied, from the redesign of the component and its installation, to the application of surface coatings with high technology materials. The main objective of this work is tribological analysis of cavitation in AISI 1020 steel samples, coated by termal spraying with Tungsten Carbide and later irradiated by CO2 Laser. The samples were analyzed by SEM/EDS, Optical Microscopy, Rugosimeter, Vickers Microindentation hardness and cavitation resistance. The results were a metallurgical bond between coating and substrate, in addition to densification and surface hardening of the coating due to CO2 laser remelting; The EDS analysis of the substrate and its coating shows the evaporation of more volatile elements such as Chromium and Cobalt at the time of Laser irradiation, and confirms the diffusion of chemical elements of the coating on the substrate; There is a decrease in surface roughness after termal spraying coating. The cavitation test, shows that samples are resistant to erosion cavitation, proof to be superior to commercial materials.
Keywords: Engenharia mecânica
Aspersão térmica
Cavitação
Aço AISI 1020
Mechanical Engineering
Thermal Spraying
Cavitation
AISI 1020 steel
metadata.dc.subject.cnpq: CNPQ::ENGENHARIAS
metadata.dc.language: por
metadata.dc.publisher.country: Brasil
Publisher: Universidade Federal do Pampa
metadata.dc.publisher.initials: UNIPAMPA
metadata.dc.publisher.department: Campus Alegrete
Citation: RONZANI, Antonio Guilherme. Resistência à cavitação do revestimento de carbeto de tungstênio refundido via laser de CO2 aplicado em aço AISI 1020. 101p. 2017. Trabalho de Conclusão do Curso (Graduação em Engenharia Mecânica) - Universidade Federal do Pampa, Campus Alegrete, Alegrete, 2017.
metadata.dc.rights: Acesso Aberto
URI: http://dspace.unipampa.edu.br:8080/jspui/handle/riu/1913
Issue Date: 4-Jul-2017
Appears in Collections:Engenharia Mecânica

Files in This Item:
File Description SizeFormat 
ANTONIO GUILHERME RONZANI - 2017.pdf2,5 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.